PENGARUH FRAKSI VOLUME TERHADAP KEKUATAN TARIK DAN LENTUR KOMPOSIT RESIN BERPENGUAT SERBUK KAYU
Abstract: On the research,
composite was made from polyester with volume of filler fraction variable of 15%,
30%, 45% and
the type of
filler was Mahogany
(Swietania mahogani). The
filler measurement used was
50 mesh. Polymer
matrix used was BQTN 157
unsaturated resin polyester. The
tensile test of experiment specimen was based on ASTM D638 M-93. and the bending specimen
was based on
D790-92 Standard. The
higest of tensile
strength on the volume fraction of 30% that is of 2.081916
kg/mm2. For the composite material with particle of composite material
mahogany with filler
volume fraction of
15% had the
average flexural strength of
34.98 N/mm². On the particle with volume fraction of 30% had the highest
average flexural strength of 45.6780 N/mm². The higest Modulus of Elasticity(E)
and Shear Modulus (G) was owned by the composite with filler volume of 635.464
kg/mm2dan 958.85 MPa
Penulis: Femiana Gapsari, Putu
Hadi Setyarini
Kode Jurnal: jptmesindd100169