KARAKTERISTIK BATAKO DARI CAMPURAN SEMEN DAN SERBUK GERGAJIAN KAYU PALAPI (HERTIERA SP)
ABSTRACT: This research was
conducted on February up to the month of
May 2015 in Machine Laboratory of Technique Faculty and Forestry
Laboratory of Forestry Faculty of Tadulako University. The research steps were
preparing material, making sample and testing sample. This research applied
Complete Random Design with 5 repetitions and treatments, they were comparison
of cement and sawdust composition that consisted of 4;1:1, 1:3, 1:5 and 1:7.The
result of the research showed that the comparison rate of adobe water
absorption was on 1:1 (17%), 1:3 (54%),
1:5 (61%), 1:7 (71%). Fault strength was on 1:1 (2,907 kg/cm2), 1:3 (0,956
kg/cm2), 1:5 (0,822 kg/cm2), 1:7 (0,975 kg/cm2) comparison. Bending Strength
was on 1:1 (10,914 kg/cm2), 1:3 (3,911 kg/cm2), 1:5 (3,197 kg/cm2), 1:7 (3,135
kg/cm2). Pressing Strength was on 1:1 (25,4 kg/cm2), 1:3 (5,88 kg/cm2), 1:5
(2,9 kg/cm2), 1:7 (3,13 kg/cm2).
Kata kunci: Palapi wood,
Sawdust, Adobe
Penulis: Nuryanto Hafid
Wahyudi, Erniwati, Abdul Hapid
Kode Jurnal: jpkehutanandd170160