PENGARUH PERLAKUAN PANAS BAJA AISI 1029 DENGAN MEDIA PENDINGIN AIR DAN OLI TERHADAP KEKUATAN DAN KEKERASAN
Abstract: The process of heat
treatment is a combination of the operation of heating and cooling with certain
speed and was conducted on metal or alloyed in the solid state as an attempt to
acquire the nature of certain properties. The temperature of the warming is
done for 7850C and 8200C. As for the purpose of this research is to find out how
the mechanical properties of steel heat treatment at different temperatures and
then to find out the value of the
strength and hardness
of steel with
optimal cooling water
and oil media.
research methods used
are experimental methods, experimental
group consisted of
samples which have
been subjected to
heat treatment which is
pull-test sample amounted
to 13 sample
afterward for comparison
is 3 samples.
How does the difference in strength and violence that
occurred after the heat treatment was given with water cooling and oil media
against material that had not been given the treatment. From the test results
and calculations made on the influence of heat treatment of Steel AISI 1029
with water cooling and oil mediums of the strength and hardness, the highest
strength values found in the samples that were given a heat treatment at a
temperature of 8200C with the value of the strength
value then Mpa
972 highest violence
also occurs in
the sample who
were given preferential treatment
at a temperature of 8200C with 299 VHN.
Penulis: Nofriady Handra dan Rio Fernando
Kode Jurnal: jptmesindd140216