PENGARUH PENAMBAHAN FRAKSI BERAT ZIRCONIA TERHADAP SIFAT FISIK DAN MEKANIK KOMPOSIT ALUMINIUM DIPERKUAT ZIRCONIA YANG DIPRODUKSI DENGAN METALURGI SERBUK
ABSTRACT: This research aims
to utilize zirconia (ZrO ) as a reinforcement of aluminum matrix composite
(AMC). ZrO 2 2 powder of 0%, 2.5%, 5%, 7.5%, 10%, 12,5%, and 15% wt were added
to fine aluminum powder (dimension of particles are smaller than 40 μm). Each
composition was mixed using a turbula mixer for 2 hr. The mixture was
uniaxially pressed with a pressure of 300 MPa to produce green bodies. They were
pressure less sintered in argon atmosphere at temperature of 600ºC. Relative
density, Vickers hardness, and bending strength of the AMC were tested. The
results show that the hardness increases with increasing the ZrO content up to
5% wt whereas wear rate decrease. Relative density and Vickers hardness of
composite containing 5% ZrO2 are 89%, 34 HV15 and 0.076 mg/(MPa.m),
respectively. Maximum bending strength was reach on 7,5% ZrO adding on 37,66
MPa.
Penulis: Bayu Satriya Wardhana
Kode Jurnal: jptmesindd140204