PENGARUH TEMPERATUR TERHADAP SIFAT MEKANIK PADA BAJA KARBON SEDANG ST 60
ABSTRACT: Medium carbon
fertilizer ST 60 in general
is often used
in construction of building
materials and a
variety of fields.
Society prefers medium
carbon fertilizer because this
material is more
easily available and
relatively affordable
prices, and also
the strength and
tenacity are sufficient. Temperature significantly affects
the mechanical properties of carbon steel is ST
60. Formulating of
the problem in this
study is to
determine how the mechanical properties
of medium carbon
steel ST 60
to temperature 00C, 260C, 500C,
1000C. The purpose of this research to know how much testing on tensile
strength, hardness, and price impact. The results of research on testing with 00C yield
of 696,68 N/mm2 tensile
test, hardness test
of 201,00 HB,
the impact test produces
30,35 J/cm2. In
the test with
a temperature of 260C
produced by 694,47
N/mm2 tensile test,
hardness test of
200,11 HB, the impact test at 24,52 J/cm2. In
the test with a temperature of 500C produced by 685,87 N/mm2
tensile test, hardness test of 198,00 HB, the impact test at 41,70 J/cm2. In
the test with
a temperature of 1000C resulted
N/mm2 tensile test
at 672,89 N/mm2, the
hardness of 195,56
HB, the impact
test at 37,69
J/cm2. Data
analysis in this
study using the
product moment correlation
test and t-test.
The conclusion of
this research is
that there is
a negative relationship between temperature with
mechanical properties which means the higher the temperature the
more down the
value of tensile
strength, hardness, and
the price impact.
Penulis: Lagiyono, Suwandono,
Mukhamad Masykur
Kode Jurnal: jptmesindd110249