PENGARUH WAKTU GESEK FRICTION WELDING TERHADAP KARAKTERISASI BAJA AISI 1045 DENGAN SUDUT CHAMFER 15 DERAJAT
ABSTRACT: Friction welding is
a technique by rubbing between two metal surfaces to produce a heat source,
causing the union between the two metal surfaces without using filler metal.
The purpose of this research is to improve the mechanical strength of metal
welded joints 1045. The research method is done by rubbing between the two
metal surfaces with the time variation of friction 25 seconds, 35 seconds, 45
seconds and 55 seconds. Friction time in 45 seconds able to get the highest
tensile strength about 703,835 N/mm 2
and get fracture in main metal. In other, at the time of friction 25
seconds reach its low tensile strength about 429,671 N/mm 2 and occured a fracture in connection welds.
Best hardness distribution obtained at the time of friction 55 seconds with a
value of 270 BHN in hardness weld metal, the hardness value inleft part of HAZ
reach 252 BHN and hardness value of right part of HAZ reach 247.6 BHN. Lowest
hardness obtained at Friction time in 25 seconds with welding metal hardness of
250 BHN, hardness value in left side HAZ reach 240.3 BHN and the right sideof
reach 236.6 BHN. Time friction affect to the microstructure and mechanical
properties of AISI 1045. Smaller crystal structure will be block the movement
of the dislocation, so that the mechanical properties of the metal are getting
better, and conversely when crystal structuresare formed getting greater, the
mechanical properties of the material will decreases.
Penulis: Riko Septian, Gaguk
Jatisukamto, Salahuddin Junus
Kode Jurnal: jptmesindd160341