Pengaruh Tekanan Kompaksi Pressure Sintering Terhadap Ketahanan Impak Dan Kekuatan Tarik Limbah Kemasan Aluminium Foil
Abstract: Aluminium foil
sachet waste has potential to becomes the eco friendly alternative materials.
This research aims to investigate the effect of compaction pressure toward the
characteristics of aluminium foil sachet waste. The used method was pressure
sintering, where pressing temperature maintained at 135 oC and holding time of
10 minutes . The used of compaction pressure was divided into 2 bar, 4 bar, 6
bar, and 8 bar. The tested
mechanical properties were
impact test and tensile test.
The result shows the addition of compaction pressure will increase the
tensile strength, while
the impact strenght decreased. Compaction pressure test
at 8 bar showed the highest tensile strength value of 9,01 Mpa and compaction
pressure test at 2 bar showed the highest impact strength value of 21,78 Mpa.
Penulis: Erwan Setya Putra,
Heru Sukanto, Purwadi Joko Widodo
Kode Jurnal: jptmesindd160691