OBSERVATION PARTICLE SIZE OF MG0.8ZN0.2TIO3 BY LASER DIFFRACTION METHOD
Abstrak: Observation of
particle size in the sample Mg0.8Zn0.2TiO3 (MZT) calcined at 550oC with various
holding time 1 hour, 2 hours, 4 hours and 6 hours has been done. The results of
X-ray diffraction analysis showed that the formed phase is geikelite (MgTiO3) and
rutile (TiO2), which indicates that there had been reaction between Zn and Mg.
This research aim to know size distribution of particles in colloidal using
laser diffraction method based on principle dynamic light scattering. The
average particle diameter measurable each sample ZMT is 310.1 nm, 313.9 nm,
334.2 nm and 365.4 nm which states that the longer the holding time resulted in
increase grain size particles.