FABRIKASI DAN PENGUJIAN TARIK PIPA KOMPOSIT BERPENGUAT SERAT WOL DENGAN ADITIF PARTIKEL MONTMORIILLONITE
Abstract: Composite is one
kind of material created by the merger of two or more kinds of materials that
have different properties into one new materials with different properties.
Composites are also widely used in the automotive industry. The use of
composite particles of montmorillonite (MMT) is expected to contribute to the
development of alternative materials made from clay. The purpose of this study
was to determine the effect of particle size variation of the value of the
tensile strength of the pipe Composite wool fibers with additive MMT particles,
determine the effect of particle size variation of the morphology Composite
pipe wool fibers with additive MMT particles after the drop test. The method
used is the method of filament winding. For the testing standards used for
tensile tests using ASTM D 2290. From the test results can be concluded that
there are significant variations in particle size (MMT) against the tensile
strength values with an average value of 20 = 49.08 MPa mesh, mesh 40 = 63.86
MPa, mesh 60 = 107.21 MPa, 138.78 MPa = 80 mesh, 100 mesh = 167.58 MPa, 120 =
190.05 mesh, mesh 150 = 210.89 MPa.
Penulis: Ibrahim Tri
Statistianto, Agus Triono
Kode Jurnal: jptmesindd160366